This may be something you checked or knew before coming on the 'net, but I have to mention just in case: Silver oxide is electrically conductive.
 
How well compared to elemental silver I don't know and I don't have a reference to hand. I think it might be worth checking  and/or ensuring that this is an oxide problem before you go down the road of trying to remove  from assembled boards as I the only ways I can think aren't attractive.
 
If different pin profiles don't work then the alternatives  are
Chemical de-oxiders: would seem to be out on the grounds that immersing the boards in aqueous acids and rinsing them off is off limits (unless you are using water wash chemistry in your flux/paste).
 
Use flux: Possibly you could paint on flux, reflow and either probe through the residues (some fluxes allow this). Or remove flux residues. The thinking is that fluxes are an assembly product and therefore "safe"at this stage, and the oxides must be reduced by  flux well enough to solder -  this might be good enough to produce a positive test.
 
Abrasion: locally abrade the test points.
 
And that's it ..... unless other 'netters know better.
 

Regards

Mike Fenner

Applications Engineer, European Operations
Indium Corporation
 T: + 44 1908 580 400
M: + 44 7810 526 317
 F: + 44 1908 580 411
 E: [log in to unmask]
W: www.indium.com 
Leadfree: www.Pb-Free.com

-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Sherif Refaat
Sent: Wednesday, January 08, 2003 3:35 PM
To: [log in to unmask]
Subject: [TN] Immersion Silver oxidation

Hi Technetters,
 
I've got a situation here where boards coated with Immersion Silver were partly assembled before the Holidays and the assembly was completed this week. So, the boards were left in the factory, uncontrolled environment, for over two weeks. The circuitry on the side that was assembled first exhibits oxidation. The oxidations does not allow the In-Circuit test probes to have good contact with the test pads, hence causing lots of false opens.
 
Any recommendations regarding how to remove Immersion Silver oxidation from assembled boards? The Immersion Silver Chemistry supplier is located overseas and because of the time difference I can not get an immediate answer. I heard about a more pointy test probes that may be able to penetrate the oxidation but the factory does not accept this solution.
 
Can any one help?
 
Thanks in advance.
 
Sherif,
 
--------------------------------------------------- Technet Mail List provided as a free service by IPC using LISTSERV 1.8e To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/html/forum.htm for additional information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315 -----------------------------------------------------
--------------------------------------------------- Technet Mail List provided as a free service by IPC using LISTSERV 1.8e To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/html/forum.htm for additional information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315 -----------------------------------------------------