Alejandro,
 
We are currently looking into attaching the metal body of a SO8 component to a pcb. Are you able to tell me whether or not you are using a stepped stencil or a standard one, in order to acheive the required connection with the body of the device to the PCB and also and the leg to the PCB ?. At the moment we are using .006" thick stencils.
 
Regards
 
Steve. 
-----Original Message-----
From: Becerra Alejandro [mailto:[log in to unmask]]
Sent: 25 April 2002 14:11
To: [log in to unmask]
Subject: Re: [TN] Repair of Circuit with Solder Paste below

We deposit solder paste under the component in order to help for heat transfer.
The bottom side of the component is made of metal, then when I remove the component we also remove the solder.
Applying solder paste again in the rework operation is a good idea.
Do you know how can we apply solder paste during rework?
Is it possible to use a mini-stencil? Where can I find a vendor for the mini-stencil?

Thanks for your help.

Alejandro

-----Original Message-----
From: Marsico, James [mailto:[log in to unmask]]
Sent: Thursday, April 25, 2002 6:10 AM
To: [log in to unmask]
Subject: Re: [TN] Repair of Circuit with Solder Paste below


If I understand correctly, you deposit solder paste under the component
during the initial build.  After reflow, the paste solidifies and makes
contact with the bottom of the component for heat transfer.  Your question
is what to do when replacing the component.  How do you replace the solder
bumps under the device.

Is the body of the component ceramic or metal?  If ceramic, when you remove
the devise the solder bumps should remain intact, nice and flat.  Why not
leave these bumps as is and place the component, contacting the existing
bumps while soldering?  If the case is metal, and you disturb the bumps
during removal, how about reapplying solder paste, placing the component and
reflowing it with a hot air terminal?  Another option is to change the
drawing to allow the use of a thermal adhesive for rework.

Jim Marsico
Senior Engineer
Production Engineering
EDO Electronics Systems Group
[log in to unmask] <mailto:[log in to unmask]>
631-595-5879


        -----Original Message-----
        From:   Becerra Alejandro [SMTP:[log in to unmask]]
        Sent:   Wednesday, April 24, 2002 4:54 PM
        To:     [log in to unmask]
        Subject:        [TN] Repair of Circuit with Solder Paste below

        Hello to All,

        We have a circuit that requires solder under it because in order to
have a good thermal dissipation.
        The circuit is a QFP48. When assembled in the line, the stencil has
apertures in the body of the component in order to apply solder.

        We have tried to manually apply the solder with an iron tip, but
after cross-sectioning the repair component we have found that

        sometimes the solder is not in contact with the component.
        What could be the appropriate procedure to repair this component?

        Regards,

        Alejandro Becerra



---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------


________________________________________________________________________
This e-mail has been scanned for all viruses by Star Internet. The
service is powered by MessageLabs. For more information on a proactive
anti-virus service working around the clock, around the globe, visit:
http://www.star.net.uk
________________________________________________________________________