Does someone know if there is an IPC standard for a SMT Ceramic Resonators which has Castellated Terminations? Does IPC require a good Castellated fillet on both sides of the part even though the pad is continuos? On the middle pad we are getting good wetting on one of the Castellated terminals. However the other side does not have a good fillet. I feel that since the part has a pad all the way underneath itself, that a good Castellated terminal one side means that the bottom pad is also soldered. I guess the question I am asking is, according to IPC do Castellated Terminations (section 12.2.4 of IPC-A-610 C) only apply to Leadless Chip Carriers or any part that has a castellated terminal. Any help on this would be greatly appreciated. Thanks, Brad Mecham --------------------------------------------------------------------------------- Technet Mail List provided as a free service by IPC using LISTSERV 1.8d To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives Please visit IPC web site http://www.ipc.org/html/forum.htm for additional information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315 ---------------------------------------------------------------------------------