Hi Phil,
Be careful with BeCu; not all that is out there has good solderability.
Particularly beware of Cu flash over plating or tin/lead plating (even when
it is reflowed), because the underlying BeCu surface may not wet properly.
Werner Engelmaier

##############################################################