Steve, In using the OMIKRON in particular, have there been any oxidation issues for boards left in stock that would determine a life span caveat for this process. Is staining an issues for you based on the quality of the final rinse or does it matter in your process window. How has your incidence of de-wetting due to surface contaminants been wit WIT? Would appreciate hearing you experience. Charlie McMahon ----- Original Message ----- From: Steve Collins <[log in to unmask]> To: <[log in to unmask]> Sent: Monday, February 28, 2000 12:58 PM Subject: [TN] Immersion Tin > We are using White Tine on one of our boards and it is working out just fine for > us it's a 4 layer MC-5 (GIL) construction. The reason for us using this finish > is that we did not want to subject the PCB to the extreme temperature of the > HASL environment. Some of the benefits are a flatter PCB at incoming inspection > flatter pads due to the unevenness of the HASL finish. We did go through some > growing pains since we were told it was a drop in finish for HASL and found out > that we needed to tweak considerably the profiles and the fluxes. To date we > have seen no drawbacks and we have around 11000 boards in the field. We ran > DOE's on both the Omikron & Dexcoat versions with no differences found in our > assemblies. > > Hope this helps. > > Steve > ---------------------- Forwarded by Steve Collins/Antec on 02/28/2000 10:35 AM > --------------------------- > > > Russell S Gregory <[log in to unmask]> on 02/25/2000 12:12:24 PM > > Please respond to "TechNet E-Mail Forum." <[log in to unmask]>; Please respond to > [log in to unmask] > > To: [log in to unmask] > cc: (bcc: Steve Collins/Antec) > Subject: [TN] Immersion Tin > > > > Dear All, > > I am interested in the benefits of Immersion Tin as a final finish. > Do any of u use Immersion Tin as a final finish? > Why do u use it and what did u change from? > > What are the benefits for you of an Immersion Tin? > > What are the drawbacks? > > Does an Immersion Tin have to pass a specific test for approval? > Do all Immersion Tins give u the same benefits? > > Russ Gregory > > ############################################################## > TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c > ############################################################## > To subscribe/unsubscribe, send a message to [log in to unmask] with following text > in > the body: > To subscribe: SUBSCRIBE TECHNET <your full name> > To unsubscribe: SIGNOFF TECHNET > ############################################################## > Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional > information. > If you need assistance - contact Keach Sasamori at [log in to unmask] or > 847-509-9700 ext.5315 > ############################################################## > > ############################################################## > TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c > ############################################################## > To subscribe/unsubscribe, send a message to [log in to unmask] with following text in > the body: > To subscribe: SUBSCRIBE TECHNET <your full name> > To unsubscribe: SIGNOFF TECHNET > ############################################################## > Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional > information. > If you need assistance - contact Keach Sasamori at [log in to unmask] or > 847-509-9700 ext.5315 > ############################################################## > ############################################################## TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c ############################################################## To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body: To subscribe: SUBSCRIBE TECHNET <your full name> To unsubscribe: SIGNOFF TECHNET ############################################################## Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional information. If you need assistance - contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315 ##############################################################