Hi Ramsey,
Did you eliminate the problem? What's the fix?
We have wanted to switch to a water soluble mask. This might be the
perfect 'motivation' for me to do a validation test.
Hans
> We experienced intermittent corrosion after wave solder at land patterns
> that had been protected by temporary latex solder mask. We discovered
> that the natural latex, low ammonia, types were less conducive, but
> would still produce corrosion.
> The variable in the process seems to be thickness. The mask should be
> applied in as thin a layer as possible. Thick mask must trap ammonia
> under the mask. Baking a thick layer of the mask seems to make the
> problem worse. Since the mask skins over the board and protected land
> pattern are baked in ammonia corrosion results.
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
|
|
|