Subject:
From:
"Stephen R. Gregory" <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Mon, 1 Nov 1999 23:22:23 EST
Content-Type:
text/plain
Parts/Attachments:
text/plain (38 lines)
Hi ya'll,

Not to start another thread about something that will upset people, but
lately in the media there has been some talk about Kapton (tm) materials
being somewhat unstable at elevated temperatures...there's stories about this
with the recent crash of Egypt Air flight 990...

I, as undoubley as possibly many of you, have always understood that Kapton
(tm) tapes are what you should use when high temperatures are encountered.
I've used it on numerous assemblies to in the past to prevent such things as
a metal connector body connecting to a via that was mistakenly laid-out
without mask beneath the footprint. As a big as a pain in the butt as it was,
we would cut a teeny piece of kapton (tm) tape to cover a via so that there
was no chance of a via to short to the connector. This is just one
example...there have been many other instances in the past (crystals,
oscillators, etc..) or with other components where I've used Kapton (tm) tape
to do similar things...the tape needed to stay with the assembly as a finshed
product.

Should I, or designers who specify the use of Kapton (tm) in this manner be
concerned about this? Or is this just media hysteria?

-Steve Gregory-

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################

ATOM RSS1 RSS2