Paul,
The typical temperature for copper plating baths are:
Electroless copper: ranges from about 25 - 50C depending on the type (low
dep or high dep)
Acid copper: typical baths range from 20 - 30C (some high speed
baths can go up to 35 or 40C)
Hope that helps. Have a great weekend.
Joe Malley
Research Project Manager
MacDermid Inc.
PAUL BROWN <[log in to unmask]> on 10/21/99 11:47:40 AM
Please respond to [log in to unmask]
To: [log in to unmask]
cc: (bcc: Joe G Malley/MacDermid/MACDERMID/US)
Subject: [TN] Copper bath
Can anybody tell me what the average temperature of a
typical board fab copper platting bath is????????????
Thanks.........Paul
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################