What's this non tech rumble mate ? lets get back to work :
Inge, you still owe us the analysis method adopted on those intermittents
you battled with (please) .
I'd love to know if that dye line worked ; or whatever else .
And , Kelly, the minute traces of Darjeeling tea in bulk of Jamaican rum
compromised in my grog (heated capped) should not sway you to deluded
assumptions.
Otherwise I agree with you ; takes a seriously confused lord to "improve"
otherwise decent tea with something like bergamon oil, some of us use as a
solvent (orange , ok , close enough).
And Swedes boil tea in milk !
As Carey says 'enough blabbering'
paul
PS
the PCB manufacturing saga was most enlightening ; thanks fellows
PPS
Do you have a picture Ioan , of that "cold" joint ?
-----Original Message-----
From: Kelly M. Schriver [mailto:[log in to unmask]]
Sent: Wednesday, 6 October 1999 8:46
To: [log in to unmask]
Subject: Re: [TN] Cold solder
Watch it Earl - that stuff'll rust your bloomin' plumbing!! For all I know,
that might be what's wrong with our Aussie friend.
Best -- Kelly
-----Original Message-----
From: pod <[log in to unmask]>
To: [log in to unmask] <[log in to unmask]>
Date: Tuesday, October 05, 1999 12:37 PM
Subject: Re: [TN] Cold solder
>I resemble that remark.
>
>Earl Grey Great Tea
>----- Original Message -----
>From: Ingemar Hernefjord (EMW) <[log in to unmask]>
>To: <[log in to unmask]>
>Sent: Tuesday, October 05, 1999 9:52 AM
>Subject: Re: [TN] Cold solder
>
>
>> Earl Grey is a good tea, I agree,
>> Now, Joan, are you sure it's about cold soldering at all? As you describe
>it could as well be dewetting. If it's dewetting, your trouble shooting can
>leave the wavesolder for a while. Again, I wonder why you don't do a
wetting
>test on the terminals.
>> Good Lunch
>> Ingemar Hernefjord
>> Ericsson Microwave Systems
>>
>> ----------------------------------------------------------------------
>> Earl and all,
>>
>> the soldering was a lot better before. We've always had the QA on our
>back,
>> checking the flux density and the settings for the problem assemblies.
>> Myself, I don't recall having seen so much cold solder.
>>
>> The machine had been calibrated last saturday during the monthly
>> maintenance, when the pot is thoroughly cleaned.
>>
>> It's possible that the solder mask changed, since it's darker now.
>Together
>> with the soldering problems we started experiencing discoloration of the
>> solder mask on the solder side. But wouldn't this randomly affect any
>place
>> on the surface? I still get the connectors OK, with bad solder joints on
>the
>> caps and resistor networks.
>>
>> There has been no artwork change. However, could some changes in the
>> materials or manufacturing of the board affect somehow the thermal mass
>here
>> and there? I mean, maybe the connectors drain somehow the heat from the
>> adjoining components.
>>
>> And anyway, what on earth generates cold solder in the waving process?
>>
>> Ioan
>>
>> ##############################################################
>> TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
>> ##############################################################
>> To subscribe/unsubscribe, send a message to [log in to unmask] with
>following text in
>> the body:
>> To subscribe: SUBSCRIBE TECHNET <your full name>
>> To unsubscribe: SIGNOFF TECHNET
>> ##############################################################
>> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
>additional
>> information.
>> If you need assistance - contact Gayatri Sardeshpande at [log in to unmask]
or
>> 847-509-9700 ext.5365
>> ##############################################################
>
>##############################################################
>TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
>##############################################################
>To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in
>the body:
>To subscribe: SUBSCRIBE TECHNET <your full name>
>To unsubscribe: SIGNOFF TECHNET
>##############################################################
>Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
additional
>information.
>If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
>847-509-9700 ext.5365
>##############################################################
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
|