Richard, please send the photos you describe below. We have also considered
replacing electroless with direct metallization, but I have already been
down the road where fancy expensive equipment had to be yanked in favor of
simple dip lines, and I have been fighting the change. I greatly appreciate
your sharing this story with Technet.
Connie Huffman
Process Chemist
Avionics Production Division
Warner Robins Air Logistics Center
> -----Original Message-----
> From: Richard Mark Mazzoli [SMTP:[log in to unmask]]
> Sent: Friday, October 01, 1999 06:28
> To: [log in to unmask]
> Subject: [TN] Direct Plate
>
> DIRECT PLATE PITFALLS
>
> IS IT REALLY AS ROBUST AS ELECTROLESS COPPER?
>
> RICHARD MAZZOLI
>
>
> BACKGROUND STORY
>
> Recently there was a shop that was interested in replacing their
> electroless
> copper with one of the new alternative methods making all the headlines.
> They interviewed prospective vendors, listening to the good and bad points
> of
> each system on the market; some had long processing lines, some were
> relatively unproven, and some were just poorly supported or represented in
> their part of the country.
>
> Decisions were made to test one supplier's product based on a number of
> factors such as 1) it was a "tried and proven" process boasting "millions
> of
> square feet" of high quality boards, 2) a name-brand supplier to the
> industry
> made the process, 3) product support was considered to be the best
> available
> and 4) the equipment and pricing was in line. Testing commenced when the
> equipment was installed.
>
> Test data, as is often the case, was conflicting. Basically, in order for
> this process to be approved it had to stand up to 500 thermal cycles in a
> liquid-to-liquid chamber. Tests showed that if 1 mil of copper was plated
> on
> test panels there would be a 1% to 10% failure rate. A separation would
> develop - the boards would develop circumferintial voids at the oxide
> interface of the inner layers. So, the process supplier and the board
> shop
> mutually decided to test the panels with 2 mils of copper. Subsequent
> results were good (no separation occurred) and the board shop's largest
> customer approved the process based on the latest tests.
>
> The shop soon switched over to the new direct plate process and threw out
> their old electroless copper line. Cycle times were reduced, some
> unhealthy
> chemistry was eliminated and everyone was happy. Until field failures
> began
> turning up.
>
> The shop's largest customer began to find a significant number of failures
> due to open circuits. Analysis showed them to be wedge voids. Things
> went
> from bad to horrible as the shop scurried to find a solution. They began
> a
> series of tests designed to find the cause of the voiding and, more
> importantly, how to stop it. They began extensive quality checkpoints
> using
> many times the normal amount of destructive testing out of copper plating
> in
> an effort to filter out these escapes. Tests were conducted to find out
> how
> they could escape from electrical test.
>
> Of course, to the customer, all of these efforts were exercises in
> futility.
> They understood the PCB shop's problem but had problems of their own. The
> customer was quickly moving to the decision of canceling all orders and
> putting the shop on a "no order" status. They were out of patience and
> had
> their own business to protect. The PCB shop took 60 days to discover the
> cause of the defects and construct a more robust process. Too long in
> this
> day and age - the customer replaced them. All orders ceased. The shop
> replaced the direct plate process for electroless. Too little, too late.
> Several months later the shop filed for protection under bankruptcy laws.
> One year later they closed their doors.
>
> If this story sounds like fiction to you, then you'd be wrong. It
> happened.
> Of course, this is only the abridged version. The lessons learned by this
> shop have left an indelible mark on its personnel. The tests that
> resulted
> from the 60 days of failure analysis and trials have been reconstructed
> here
> so that other PCB shops might not make the same mistakes.
>
> THE FAILURES
>
> Figure 1 shows an example of the failures this study evaluated. This PCB
> has
> been thermally cycled in a liquid-to-liquid chamber for 500 cycles.
> Figure 2
> shows the same sort of defect observed at only 100 cycles. Failures were
> found at 50 cycles as well. It's important to note that these same parts
> passed original electrical test then failed after cycling. There were not
> many failures per board. In fact, out of more than 2,000 holes only 2 to
> 4
> holes would fail. Finding this level of defect is akin to stumbling
> across
> the proverbial needle in a haystack.
>
> There were many questions. What is the exact cause? How to stop them?
> How
> to detect them? Oddly enough it was only on certain board types although
> all
> board types were being processed through direct metalization. Why were
> these
> parts different?
>
> A study was conducted to determine what was different about these parts.
> Taken into account was:
>
> § Hole size
> § Aspect ratio
> § Drill type
> § Drill supplier
> § Material and pre-preg style
> § Lamination techniques
> § Drill parameters
> § Material supplier
> § Layer count
> § Process differences between these and other parts
> § Sequential lamination techniques
> § Unique board features
>
> Analysis showed that there was no difference in these boards than any
> other
> product being built except that the failed parts had non-functional pads.
> But
> other than that, there were no common features that could have accounted
> for
> the failures being only on these particular PCB's.
>
> THE NATURE OF THE BEAST
>
> This direct plate process uses a micro-etch as its final chemical bath,
> followed by a rinse then dry. Panels are then ready for dry film coating.
> This micro-etch bath is to remove the metalized coating from the copper
> surfaces - outer layers surface and interconnections. During failure
> analysis several indications pointed to this portion of the process as
> being
> a major cause of concern. A good many boards were found to have slight to
> moderate negative etchback. A "wedge" or crevice was formed at the top
> and
> bottom side (the oxide and base side) of the interconnects. It was at
> these
> places that failures would occur.
>
> Controlling the micro-etch bath in a direct plate process is easier said
> than
> done. It's not as simple as most other micro-etch baths since it relies
> on
> impingement to work. The spray actually has to get underneath the
> metalized
> coating in order to "lift" it off by removing the copper underneath it.
> In
> that manner it remains on the non-copper areas - the areas it is intended
> to
> metalize. Understanding this, it's not hard to comprehend that there is
> going to be some amount of copper missing from corners (knees) of
> interconnects and surface copper where it meets the resin/glass. This
> "gap"
> is normally miniscule. But nevertheless, it exists even under the best of
> circumstances. It is the nature of the beast. Fundamentally it becomes a
> non-conductive portion of the hole that must be plated. The only way this
> can happen is by current "jumping" the gap. Copper must literally bridge
> across this fissure and make connection to the interconnecting foil.
>
> Figure 3 shows a drawing of this copper removal. Further, it shows how
> this
> condition can become amplified when coupled with any amount of nail
> heading
> from drill. It's not hard to imagine the metalized coating being removed
> by
> the undercutting action of the sprayed-on micro-etch. It stands to reason
> then that when the copper interconnects have been, in effect, "widened" by
> nail heading that the resulting removal of the copper will now leave an
> even
> longer gap. The normally miniscule fissure now becomes even harder to
> plate.
> The fissure now becomes a full-blown gap - a break in continuity.
>
> Direct metalization works by way of a "moving front". Copper travels from
> each surface, through the holes until it "meets" (Figure 4). This is
> commonly referred to as initiation. When the moving front meets,
> initiation
> occurs and you have successfully encapsulated the hole wall and begin to
> build thickness evenly. Until that point of initiation, copper is
> building
> in thickness on areas that are conductive but obviously not on other areas
> -
> like the fissure. A wedge-like formation begins to develop which can be
> miniscule to very wide, depending on how large the non-conductive fissure
> is.
>
>
> Conversely, electroless copper has no fissure issues since it completely
> encapsulates the interconnect, resin, glass and surfaces. It begins to
> plate
> thickness immediately when current is applied. No moving-front is
> involved -
> no initiation. It's already plating on all surfaces.
>
>
> NON-FUNCTIONAL PADS
>
> Rather than debate the pros and cons of non-functional pads (NFP's) the
> testing in this study included both types of designs - NFP's and
> Functional
> Pads. Like the moniker implies, NFP's are not functional in the sense
> that
> they are not connected to any other pad. They are blind pads left on by
> designers for a variety of reasons but that really serve no function
> insofar
> as electrical conductivity is concerned.
>
> Analysis on defective parts showed that it was at the NFP that the wedge
> was
> at its worst. All defects were found to be at the interconnect of a NFP.
> Further analysis verified that even after more than one hundred micro
> sections the wedge-like defect (and subsequent separation) occurred only
> at
> the interconnect of a NFP. A test vehicle was devised to prove or
> disprove
> this finding.
>
> A test coupon was developed that included functional and non-functional
> pads
> side by side. The coupon was built as an 8 layer board, one hole
> completely
> functional (linked by circuits to another pad/hole) and the next hole
> completely non-functional (all interconnects "dead"). To test the
> possible
> role of aspect ratio in the creation of the defects, hole sizes were
> gradually increased across the coupon. Tested were 5:1, 3:1, 2.5:1 and
> 1.6:1
> aspect ratios. Figures 5 and 6 show the coupon configuration.
>
> Using this design the test hoped to find plating variances between
> functional
> and non-functional interconnects and perhaps some variance due to aspect
> ratio. Since the direct plate process plated by means of the moving-front
> it
> was decided that the initiation time delay (the time the panel entered the
> plating tank and the time it actually had thru-hole contact
> surface-to-surface) was important. Going even further, it was felt that
> since the fissure/wedge created extra resistance thereby making it harder
> to
> plate, the test should include current density variables. Therefore, the
> test was outlined as described below:
>
> 1. Panels metalized with direct metalization.
> 2. Panels metalized with electroless copper.
> 3. Panels pulled from copper tank every 5 minutes and micro-sectioned
> continuing for 60 minutes.
> 4. Panels to be plated at 10 ASF.
> 5. Panels to be plated at 20 ASF.
> 6. Panels to be plated at 30 ASF.
>
> Panels were 18x24 and had numerous coupons merged into actual customer
> parts
> - the same type parts that were failing in the field. This allowed the
> test
> vehicle to be a relatively accurate representation of the exact parts that
> were failing.
>
> The direct plate supplier was invited in and asked to perform process
> audits
> on the metalization line. In fact, they assisted in generating a good
> portion of the data collected in the overall testing. No significant
> modifications were made to the process but it was optimized to their
> recommendations. Further, the copper baths were optimized for brightener,
> copper and acid content. Rectifiers were checked for throw and all
> connections on the tanks measured for connection.
>
> RESULTS
>
> The results were definite in that they clearly showed the difference in
> plating thickness between functional and non-functional pads. The
> explanation for this is that functional pads are "networked" together in
> various configurations. These networks actually assist copper plating by
> becoming conductive then "charging", thereby helping the moving front
> reach
> its initiation point. One thing was clear; wherever there was an existing
> wedge there was extra resistance and the moving front of copper was forced
> to
> somehow get across the fissure. NFP's could have actually become anodic
> (since they were isolated on both sides by the fissure), therefore
> offering
> even more resistance to the moving front.
>
> The tests were also definite in that they clearly showed the difference in
> plating thickness between direct plate and electroless copper. Repeated
> tests showed that electroless copper yielded 25% more thickness in the
> same
> amount of time. That percentage climbed to as high as 75% more when
> looking
> at holes with only non-functional interconnects.
>
> What was not expected is that the results also clearly showed the
> formation
> of the wedge voids. Pulling the parts every 5 minutes for micro-sections
> showed where the wedge started and how it eventually "bridged". What was
> even more interesting was to see the difference between the 10, 20 and 30
> amp
> current densities. As would seem clear, the lower the current density,
> the
> lower the plating. Similarly, the wedge was even more pronounced at 10
> ASF
> than it was at 30 ASF. However, with today's designs plating at 30 ASF is
> pretty much out of the question.
>
> Figure 7 shows the difference between direct plate and electroless copper
> at
> 20 ASF after 5 minutes in the plating solution. Figure 8 shows a close up
> of
> one of the interconnects from the electroless hole and direct plate hole.
> The wedge is clear on the direct plate photo. It's important to note here
> that 5 minutes in a plating solution should be building copper thickness.
> That's almost 10% of a normal 60 minute cycle. It's clear that this hole
> is
> not plating as expected.
>
> Even at 30 ASF similar test panels showed the wedge developing. But they
> also showed something interesting. On Figure 8 you'll see the wedge but
> then
> you can also see that the copper has apparently bridged the gap somewhere
> around the circumference of the hole, since copper is starting to plate on
> the other side. Or did it somehow "jump" across the gap?
>
> TEST CONCLUSIONS
>
> After repeating these tests under close scrutiny and varying the test
> conditions certain conclusions were developed:
>
> 1. Non-functional pads increased resistance when using this direct plate
> process.
> 2. Electroless copper plated better (faster and more evenly) than this
> direct
> plate process on all coupons.
> 3. Even under the best of circumstances there will be some magnitude of
> fissure (broadening into a gap or all-out wedge) using this particular
> direct
> plate system.
> 4. This direct plate system is less robust than electroless copper when
> used
> on designs with high amounts of non-functional pads.
> 5. At low current it was impossible to reliably plate NFP holes using this
> direct plate process.
>
> Does this indicate that direct plating is a poor process. Not
> necessarily.
> With hundreds of installations worldwide, there's plenty of data and
> "millions of square feet produced" to indicate it's a viable alternative
> to
> electroless copper. Does the testing described in this article indicate
> that
> direct plate has its limits? Sure, and they prove that this direct plate
> process had even more limits than what was already known. Certainly no
> one
> selling this process knew about its limitations on boards loaded with
> NFP's.
> Neither the supplier nor the engineers who installed it realized it could
> present such a problem. In this shop, direct plate was certainly no
> drop-in
> substitute for electroless copper.
>
> BACKGROUND STORY CONCLUSION
>
> The shop where this activity took place is no longer in business. The
> building is closed, equipment gone and the people are working in other
> places. The mistakes leading to this shop's demise are many. They
> include
> poor engineering practices when testing new technology, poor decision
> making
> for allowing inaccurate test data to factor into its decision to add the
> technology, poor quality control systems that allowed the failures to
> escape
> and poor overall management for allowing all of these things to happen.
> The
> author is not implying that a technology change is solely responsible for
> this shop's fall. It's simplistic to think that this one problem caused
> the
> shop to ultimately go out of business, when in fact there were many other
> reasons along side it.
>
> But the addition of this new technology should have been more thoroughly
> investigated. It had limits that even the supplier didn't know about.
> Yet
> it was sold as a drop-in replacement. That's nothing new to PCB shops.
> We've all installed products that don't work the way they are sold. That
> don't quite do what they are purported to do. Experiences such as the one
> outlined in this article should remind us to move cautiously when
> installing
> new technologies. It also reminds us that there are very few, if any,
> "plug
> and play" replacement technologies. And so it goes in this business, as
> in
> life, caveat emptor (let the buyer beware).
>
> Richard Mazzoli has been in the PCB industry for 18 years working as
> Process
> Engineer, Manufacturing Manager and Engineering Manager. He can be
> reached
> at [log in to unmask] or [log in to unmask]
>
> ##############################################################
> TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
> ##############################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with
> following text in
> the body:
> To subscribe: SUBSCRIBE TECHNET <your full name>
> To unsubscribe: SIGNOFF TECHNET
> ##############################################################
> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
> additional
> information.
> If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
> 847-509-9700 ext.5365
> ##############################################################
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.