Ed,
        We use 490F (254C) for our solder pot temperatures.  Only on rare
special occasions do we go as high as 500F (260C), and never any lower
than 490F.  (Although, at one time we previously did).  Our application
is high mix, mostly high density, high end product and always with some
chip caps on the top side.  We do not see failures with caps any more
than what is measured at a DPMO level.  (much less than 100 DPM).
        However, I do agree that the CTE of the FR-4 laminate is higher than
the ceramic cap, and higher solder pot temperature will create more
stress at the lead termination of the cap, causing cracks that can
propagate through the plates inside the cap.  The CTE mis-match is
minimized by preheating the board in the wave machine before reaching
the solder pot.  Improper pre-heat could be one of many factors causing
the failures.
        How are you conducting the test and how is the failure mode indicated?
I would like to ensure that the non-existence of failures at our
facility is not just because I don't know about them.


                        Thanks

Ryan Grant
Process Development Engineer
MCMS
(208) 898-1145
FAX (208) 898-2789
[log in to unmask]

>-----Original Message-----
>From:  Edward Hare, <SEM Lab, Inc.> [SMTP:[log in to unmask]]
>Sent:  Tuesday, August 24, 1999 8:07 AM
>To:    [log in to unmask]
>Subject:       [TN] Chip Capacitors
>
>Hi all,
>
>Thanks for all replies to my original question about chip capacitor
>failure rates.  I am currently involved in an issue where high leakage
>current failures (~300 microamps at 50V) occur at a fairly significant
>rate on chip caps that are on the top side of a mixed PTH/SMT assembly.
>SMT components are reflowed in an IR oven and then the PTH components
>are stuffed and wave soldered.  I read through John Maxwell's (AVX)
>papers and it appears that he recommends a solder wave temperature of
>232 +/- 2 degrees C for assemblies with chip capacitors.  My clients use
>a 260 degree C wave (which I have always thought was typical).  Do any
>of you follow Maxwell's recommendations?
>
>Best regards,
>Ed
>--
>
>               SEM Lab, Inc.
>Scanning Electron Microscopy and Failure Analysis
>               Snohomish, WA
>               (425)335-4400
>           http://www.sem-lab.com
>
>##############################################################
>TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
>##############################################################
>To subscribe/unsubscribe, send a message to [log in to unmask] with following
>text in
>the body:
>To subscribe:   SUBSCRIBE TECHNET <your full name>
>To unsubscribe:   SIGNOFF TECHNET
>##############################################################
>Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
>information.
>If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
>847-509-9700 ext.5365
>##############################################################

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################

ATOM RSS1 RSS2