Guru Andy - Based on your "ps": How does zinc chromate passivation fit into the general picture of copper solderability? Could it be used instead of or along with OSP coatings to reduce copper oxidation?
- LeRoy
-----Original Message-----
From: Andy Magee [SMTP:[log in to unmask]]
Sent: Saturday, July 24, 1999 8:08 AM
To: [log in to unmask]
Subject: Re: [TN] Copper oxide removal
Sulfuric is preferred over Hydrochloric for oxide removal because HCl
tends to increase in etch activity as the dissolved copper concentration
goes up with use. 10% H2SO4 will be a much more stable and reliable
process for oxide removal. Save the nitric for things like stripping
copper off your plating racks.
Andy Magee
Flex Guru - Consulting
[log in to unmask]
(937) 435-3629
ps. Initially copper foil is provided from the supplier with a zinc
chromate passivation coating to prevent oxidation. Since this angstroms
thick, relatively brittle, layer may not be uniformly intact it should
be removed with a process that will not attack the copper before
microetching. 10% H2SO4 is clearly the preferred choice over HCl, but
there are also a number of proprietary acid/surfactant mixtures that are
widely used for this.
LeRoy wrote,
Subject: Re: Copper oxide removal
Date: Fri, 23 Jul 1999 15:56:52 -0400
From: LeRoy Forney <[log in to unmask]>
My understanding of the usual oxide removal procedure is a 3-minute soak
with 5%HCl. The goal is a very mild
etch, and I've heard that nitric acid will cause pitting instead - and
this is in line with some laboratory
oxidation studies I did some time ago. Variability in solderability
data was much higher on aged coupons I had
treated with dilute HNO3 than on coupons treated with 5%HCl.
LeRoy
-----Original Message-----
From: nishath yasmeen [SMTP:[log in to unmask]]
Sent: Friday, July 23, 1999 3:34 PM
To: [log in to unmask]
Subject: [TN] Copper oxide removal
Hello everyone!
Is Nitirc acid ( dilute) a better acid than sulfuric for cleaning
the oxide on plated copper?
Any information provided will be appreciated.
Yasmeen
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
|
|
|