Date: |
Mon, 22 Mar 1999 08:50:46 +0100 |
Reply-To: |
|
Content-Transfer-Encoding: |
7bit |
Subject: |
|
From: |
|
X-cc: |
[log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask],
[log in to unmask],
[log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask],
[log in to unmask],
[log in to unmask],
[log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask], [log in to unmask],
[log in to unmask],
[log in to unmask] |
In-Reply-To: |
<3524526513D7D1119B0E00805F199142DE8C94@USSVML01> |
Content-Type: |
text/plain; charset=US-ASCII; name="[TN]" |
MIME-Version: |
1.0 |
Parts/Attachments: |
|
|
Hello Neal.
Try some of these sources. I have used them many years ago when we had
problems. I assume that you are aware that problems seldom occur until
you run lots of current and/or exceed +125C.
re 1: IEEE 82 Proc. IRPS "The influence of contaminations on
aluminium-to-gold intermetallics" by Charles, Romanesco et al at Applied
Physics Labs, Maryland.
re 2: IEEE 82 CH1781-4/82/0000-0421500 "Low Temperature void formation
jin gold-to-aluminium contacts" by Plunkett at Sandia Labs Albuguerque
New Mexico.
re 3:IEEE 82 CH1990-1/84/0000-0037 "Epoxy Degradation Induced Au-Al
Intermetallics void formation in Plastic encapsulated MOS memories, by
Rebecca J.Gale at AT&T Bell Labs, PA.
re 4: IEEE 91 0569-5503/91/0000-0859, "Resistance drift in Aluminium to
Gold US Wire bonds, by Robert M. Murcko et al at IBM Endicott NY.
re 5: "The resistance increase in Gold-to-Aluminium interconnects with
time and temperature" by D.W.Bushmire at Sandia Labs Alb. New Mexico
re 6: "Ambient Effects on Gold-Aluminium Bonds" by Thomas J.Rossiter at
Romw Air Development Center, Griffis Air Force Base, NY.
re 7:"Gold Aluminium Interconnect stability on Thin Film Hybrid
Microcircuit Substrates" by D.W.Bushmire at Sandia Labs, Alb. New Mexico
re 8: "Metallurgical Aspects of Aluminium wire bonds to Gold
Metallization" by James L. Newsome at Honeywell Inc Aerospace Div,
St.Petersburg, Fl.
re 9:"Failure Modes and Mechanisms in Electronic Packages" by
Viswanadham Singh. Can be ordered at [log in to unmask]
I also recommend you to speak with Erich Polzer at duPont if you want to
know what dopants should be used in the gold to reduce intermetallic
growth. His e-mail is [log in to unmask]
If you think of PWBs I'm sure you have a lot of references already, if
not try Simon Huetter at Optiprint e-mail [log in to unmask]
I suppose you are already drowned by information in the matter.
Good Luck!
Ingemar Hernefjord
Ericsson Microwave System
PS. This information is sent also to my friends within Ericsson. DS.
-----------------------------------------------------------------------
> I am looking for more recent material on the growth, care and feeding
of
> Au/Al intermetallics in gold ball on aluminum IC pad wire bonds than
George
> G. Harman's excellent though all too brief book, "Wire Bonding In
> Microelectronics" with a 1989 copyright. More specifically, I am
interested
> in known contaminants that reduce the time and/or temperature
components
> required to grow the intermetallic layer. I would also like to know
what a
> "typical" intermetallic layer thickness is, if there is such a thing
as
> typical.
>
> I would greatly appreciate if someone would at least refer me to
relevant
> material.
>
> Thank you.
>
> Neal Forss
>
> fax: (408) 738-8364
> work: (408) 522-6304
> email: [log in to unmask]
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section for additional information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312
################################################################
|
|