Paul:
Please see my response to you off-line as this is not an appropriate
place for this particular discussion.
Phil
Date: Wed, 19 Aug 1998 18:31:34 +0100
From: Paul Gould <[log in to unmask]>
Subject: Re: cupric chloride etcher controllers
Phil,
I think you are being unfair. In my opinion what Rudy said is as close
to
an
endorsement as you could expect and he is factually correct, or do you
maintain that your system will control the three parameters as
accurately
as
three independent controllers do?
I guess we are really talking about HCl and Oxidiser because you
probably
add water by SG control anyway. In my experience you have to add them in
varying amounts depending on the type of work processed and no system
which
controls both from one parameter can be as effective. If your system
adds
both in a fixed ratio then it will be more variable than using
Conductivity
and ORP controllers to add them separately as required.
This is not to say that yours is not a good system, it clearly is, but
you
have to recognise the limitations.
Paul Gould
Teknacron Circuits Ltd
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section for additional information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312
################################################################
|
|
|