Jared-

    I am not sure that heat alone is enough to burn off oxides. Also,
the stress to the components could be significant.  Would it be possible
to use a more active flux to chemically remove the oxides before the
wave until you determine if the leads are above a standard solderability
limit?

Ryan Jennens
Phoenix Engineering

################################################################