higher temperature solder pot will increase build up of copper much faster
which leads to contaminated solder.
-----Original Message-----
From: Todd Ness <[log in to unmask]>
To: [log in to unmask] <[log in to unmask]>
Date: Tuesday, June 30, 1998 3:11 PM
Subject: [TN] Wave Solder Pot Temp-63/37
Hi,
I would like to know the differences between having our solder pot
temp for 63/37 solder at 261 Degrees C instead of 250 Degrees C. Will
we see less bridging and better top-side flow at the higher temp? Are
there any pros and cons for the different temperatures?
Thanks,
Todd N
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional
information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or
847-509-9700 ext.312
################################################################
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section for additional information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312
################################################################
|
|
|