We seem to have an issue with tents breaking on large
     holes ( .180 to .250 dia. ) as well as slots, typically .118 x .250.
     No matter whose film we have tried, the tents break. It is not always
     every panel, nor every lot. We have an idea that it may be being
     caused by the developer. Has anyone out there wrestled with this
     problem, and if so how was it resolved. To switch to secondary drill
     would just impact that departments output Any help will be deeply
     appreciated.

                  Ernie Smith
                  Electropac Co. Inc.

     e-mail to   [log in to unmask]

     or on the technet

################################################################