Has anyone any information on barrel cracking associated with the use of
electroless nickel (EN) under a gold finish. We have a problem with 0.3 mm
via's in FR4 multilayer boards cracking after thermal shock at 260°C. We have
other problems with this board but is there any information on what effect EN
has under these conditions ?
Any comments ?
Thanks
Chris
################################################################