Sergio Nunez <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Mon, 16 Feb 1998 10:35:20 -0800
Content-Type:
text/plain
Parts/Attachments:
text/plain (46 lines)
Chris_Smith wrote:
>
>      All,
>        My company is contemplating switching to the sls65 flux for our wave
>      solder processes.  We are currently using Alpha Metals NR210X no
>      clean, but are not completely satisfied with the results.  A year or
>      so ago (before I came on)the company ran a 55 gallon drum of SLS65
>      flux through one of our solder waves.  From what I've heard and read
>      it was a tremendous success with eliminating solder defects (mainly
>      solder balls).  However, I myself have no history with this flux and
>      was hoping that some of you who do can give your input.  Please let me
>      know what you think.
>
>      Thanks
>      Chris Smith  M.E.
>
> ################################################################
> TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
> ################################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
> To subscribe:   SUBSCRIBE TechNet <your full name>
> To unsubscribe:   SIGNOFF TechNet
> ################################################################
> Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
> For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
> ##############################################################
Hi cris.
I prove sls65 and I have a great results to elimanate solder balls
in mother board.
you need to crontrol the spray flux & preheat zone 90 to 100 deg.c.
when i run my product i dont have more than 160 deg. in the peak
and i eliminate the solder ball.
I think this product it's good.

################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe:   SUBSCRIBE TechNet <your full name>
To unsubscribe:   SIGNOFF TechNet 
################################################################
Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
################################################################


ATOM RSS1 RSS2