Matthew Park wrote:
>
> Entek Plus data spec from Enthone specified a coating
> thickness of 0.35um (min 0.2um to 0.5um max). My pcb vendor
> follows this thickness req. and performs a UV
> spectrophotometer test as per a batch cycle to measure the
> coating thickness. (By the way the vendor uses dip-tank process
> for coating Entek-Plus) I am seeing brown residues on TH
> solder joints (not on smt solder joints after reflow) after
> wavesoldering.
>
> I am drawing a conclusion that the cause of brown residue is as
> the result of much thicker coating in plated TH holes. I believe
> heat and flux (2% no clean flux) do not have a time to dissolve
> and evaporate the coating in plated TH holes. Semi-dissolved
> coating in TH holes gets pushed up toward the component side
> by molten solder. Thus causing spotty brown residue on TH
> solder joints on the component side of boards.
>
> The reduction of belt speed (3.5ft/min) and some heat increase
> do not reduce this residue. Hand-soldering of TH holes were
> performed with the same result as per previous e-mail
> message.
>
> I wish I had a damn micrometer to measure that coating
> thickness, or Is there more stuff???
>
> regards
> Matthew Park
> NII Norsat International Inc.
>
> ################################################################
> TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
> ################################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
> To subscribe: SUBSCRIBE TechNet <your full name>
> To unsubscribe: SIGNOFF TechNet
> ################################################################
> Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
> For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
> ################################################################Matthew,
Call the company ECI. this company manufactures an instrument that can
help you measure the osp coating thickness.The principle is based on a
sequential electrochemical reduction analysis, or SERA for short.
Good luck.
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
################################################################
|
|
|