Andy;
CTE = 7-9 ppm/degree C
Dk (w/ hi temp epoxy) = 3.9
Dk (w/ polyimide) = 3.6
Tg (w/ hi temp epoxy) = 150-180C
Tg (w/ polyimide) = 210-250C
sources: Arlon, Dielektra GmbH, Isola Werke, NELTEC, and Polyclad NH
this is all from a DuPont brochure dated 2/20/96
there is a phone # for additional info: 800/453-8527
Hope it helps
Fred J.
By the way; I understand water absorbtion is a big issue with this
material (becasue of the aramid fiber).
>>> Electr1998 <[log in to unmask]> 01/16/98 09:29am >>>
Can anybody give me the following info on Thermount?
Tg
CTE
Dk
Thanks!
Andy
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with
following text in the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or
847-509-9700 ext.311
##############################################################
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
##############################################################
|
|
|