Phil,
The composition of Olin C7025 is:
Ni 3.0%
Si 0.65%
Mg 0.15%
Cu Balance
Regards,
Rob Schetty
LeaRonal Inc.
Freeport, NY, USA
----------
From: TechNet on behalf of Phil Culpovich
Sent: Monday, January 12, 1998 10:30 AM
To: [log in to unmask]
Subject: [TN] Olin 7025
Technetters:
Is there anyone using Olin 7025 that can tell me its composition? An
associate of mine is working with a lead frame manufacturer and they
would like to know what 7025 is made of so they know what to reactions
to expect throughout their processes.
Thanks
Phil Culpovich
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or
847-509-9700 ext.311
##############################################################
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
##############################################################
|
|
|