Hi Sam,
A couple of ideas to try - Shorten the dwell in the solderpot (about 1
or 2 seconds) then crank up that ascent speed. ( I know that this seems like
it would be contrary to belief) Less flux on the panel or a thinner flux
might help as well. If panels have tin on them (used as etch resist) , leave
the tin on and just flux and level at the same parameters listed above. Word
of caution though -watch that tin content and monitor the contaminant level
closely as well. Let me know how you make out.
Bob Daniels, Jr.
ECC Corp.
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
##############################################################
|
|
|