I replied to Ben Lees question and in re-reading it in daylight, found I made 
an error:

I said that temporary latex would not decompose as easily in contact with 
chemicals and solvents - NOT SO

It is the reverse. Natural latex we found to work better.

e.g. when we use it for conformal coating masking, the solvents in the 
coatings degrade synthetic latex not natural. Exhibited as easy fragmentation 
during de-mask.

Sorry about that. Shouldn't do this when je-lagged!

Graham Naisbitt