Received: |
by ipc.org (Smail3.1.28.1 #2)
id m0weKNw-000BjQC; Wed, 18 Jun 97 08:02 CDT |
Content-Type: |
text/plain; charset=us-ascii |
Old-Return-Path: |
|
Date: |
Wed, 18 Jun 1997 15:15:38 +0000 |
Precedence: |
list |
Reply-To: |
|
From [log in to unmask] Wed Jun 18 08: |
52:56 1997 |
Message-ID: |
|
MIME-Version: |
1.0 |
Status: |
O |
X-Mailing-List: |
|
>From willli Wed Jun 18 08: |
03:13 1997 |
TO: |
|
Return-Path: |
<TechNet-request> |
X-Status: |
|
X-Loop: |
|
Resent-From: |
|
Resent-Message-ID: |
<"wYgkB3.0.5rB.xnzfp"@ipc> |
Subject: |
|
From: |
|
Content-Transfer-Encoding: |
7bit |
X-Mailer: |
Mozilla 3.01 (Win16; I) |
Organization: |
netvision |
Resent-Sender: |
|
Parts/Attachments: |
|
|
Hi,Technetters!
Could anybody comment on solderablity of immersion gold on electroless
nickel ?
What is the influence of the phosphorus content on the solder joint
reliability?
Some people say that phosphorus content up to 8% is beneficial for the
solderability.I heard the opposite too.
What about having to change the reflow profile to a peak of 240
degrees in order to enhance its dissolution in solder?
And about press fit connectors in immersion gold plated holes:
Are there specifications from vendors concerning hole diameters,nickel
thickness,immersion force,aso?
Thank you,
Gaby
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To subscribe/unsubscribe send a message <to: [log in to unmask]> *
* with <subject: subscribe/unsubscribe> and no text in the body. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
|
|
|