When I worked in a manufacturing facility, we used sodium chloride in our
cupric etcher to increase etch rate.  We did experience faster wear on the
equipment using this method.  Nozzles in particular seemed to wear faster,
although we also had problems with pumps. 

You can achieve an increase in etch rate by running at a higher than usual
normality, without causing machine wear.  There is a  trade-off here as well;
normality higher than about 3.0 can attack photoresist.  If you decide to run
a high normality, I'd recommend using a system of carbon filtration.

Mark Dowding
Regional Technical Specialist
Insulectro

***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To subscribe/unsubscribe send a message <to: [log in to unmask]>   *
* with <subject: subscribe/unsubscribe> and no text in the body.          *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact   *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask]      *
***************************************************************************



ATOM RSS1 RSS2