HI,
I'd like to inquire about the supply side market for commercial grade
components that meet the requirements of IPC/J-STD-002 re. solderability
Currently we do not specify any solderability spec for the purchase of our
electronic components. We get many products that solder very well - both
wave and hand with various fluxes(no clean - RMA - OA). Some parts are not
so good - even mil spec.
After talking with our major distributors it seems that the commercial grade
parts that meet J-STD/IPC/Mil standards for solderability are not as
available as straight commercial grade and will cost a bit more. They also
said I would have to change part numbers - which would be a horrific task.
Is this true or am I talking to the wrong suppliers?
The second question is that given we do not appear to have a "problem" with
most of our straight commercial grade parts, what gains could be made by
sacrificing some cost and leadtime? No strong evidence exists that suggests
a field performance / reliability concern. I can not see how I could justify
"raising the bar", however many experts say that to change would be an
improvement.
Anyone have a practical philosophy on this dilemma that I can borrow?
Steve Ross
US&S
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To subscribe/unsubscribe send a message <to: [log in to unmask]> *
* with <subject: subscribe/unsubscribe> and no text in the body. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
|
|
|