I have not run FR-4 for a long time but that sounds like excessive movement to
me. I once worked for a laminator that made thin core and prepreg most of which
was FR-4. We also did mass lam. I believe we usually had less than 0.5 mils
movement per inch even on designs that had the worst movement.
To make the prepreg you have to drag and pull glass cloth through the treater
and so there will be movement. Talk to your material supplier about this
problem, they might suggest another construction to reduce movement. More resin
means more movement.
Good Luck
Chuck Brummer
[log in to unmask]
______________________________ Reply Separator _________________________________
Subject: FR-4 material movement
Author: [log in to unmask] at ccUnix
Date: 2/14/97 4:58 PM
My previous posting did not yield any suggestions. I'm submitting again and
hope to have responses.
>Date: Fri, 07 Feb 1997 10:25:09 -0500
>To: TECHNET
>From: sam mccorkel <[log in to unmask]>
>Subject: FR-4 material movement
>
>We experience up to .020" material movement on FR-4 materials.We ran some
tests and measured after each operation and found that it began to move after
etch, and moved a lot more after screen bakes and hot air leveling.We have
not seperated panels by grain direction in our tests so far. We've tried
baking before drilling and have not seen a significant difference from those
not baked. The movement we experience causes major problems when we rout or
score. We have to internally pin each piece to hold a =B1 .005" tolerance
between a drilled hole and the edge of the part.We used to be able to pin
externally with 4 pins to rout our boards and had no problems. Internally
pinning adds a lot of labor with panels that have many parts on them. This
problem cropped up on us about 10 months ago. Before that it wasn't a
problem. Are other fabricators out there experiencing this same problem? Is
there anything we can do to reduce the amount of movement? Should the
material move this much with "normal" processing of 2-sided boards that are
.062" thick? Do you have to internally pin each part on your panels?
>
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To subscribe/unsubscribe send a message <to: [log in to unmask]> *
* with <subject: subscribe/unsubscribe> and no text in the body. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
|
|
|