So, if you use the Ni/Au as an etch resist, what protects the trace edges
corrosion? Do you plan to plate it twice or strip the gold? I think
the photo resist is cheaper.
Chuck Brummer, Acuson.
______________________________ Reply Separator _________________________________
Subject: Gold as Etch Resist
Author: [log in to unmask] at ccUnix
Date: 1/29/97 3:35 PM
Hello,
Please post information, experiences, and anecdotes, on using
electroplated gold as an etch resist. In particular how is the etch
rate controlled. How can the undercut be reduced to eliminate the
chance of slivers.
(Gold/Nickel/Copper/FR4 :The copper gets etched)
Thanks
Rich
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
|
|
|