Hello Technetters,
I need some advises. I have a 6- layers board. I try to wave solder it,
the solder
at the ground point is not able to flow up to the top side of the board, in
fact, it
doesn't flow above 75%.
We have tried using a solder-iron and set to temperature to 450 deg. cel. and
hopefully able to force the solder through the PTH. Too bad, it didn't work
anyway
and it in fact has caused some lifted pads.
We use full blow Nitrogeneous wave-solder machine, and the flux we use is
only 1.2% solid content. And if the preheat temperature set to high, the flux
gets degraded before it even reaches the wave..
I would like to know if anyone could advise me how wave-solder such a board
with a great heavy thermal mass.
Thanks in Advance..
=-=-=-=-=-=-=-=-=-=-=-=-=-=-=-=-=-=-=-==-=-=-=-=-=-=-=-=-=-==-=-=-=-=.
/ Kong Hui Poh /
/ Techgate /
/ - The Technological Gateway - /
/ Email Add: [log in to unmask] /
/ /
/ Fax Number: (65) 842 0318 /
/
............................................................................
................................../
/_________________________________________________________________/
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
|
|
|