From [log in to unmask] Wed Dec 18 08: |
24:52 1996 |
Resent-Message-ID: |
<"NSuMK2.0.EKO.enzjo"@ipc> |
Subject: |
|
From: |
|
In-Reply-To: |
|
X-Openmail-Hops: |
1 |
Mime-Version: |
1.0 |
Message-Id: |
<H000048500abd9bc@MHS> |
Parts/Attachments: |
|
|
> but if you want to go to ENAu you will have to change your wave solder
> parameters to get good solder rise in the through holes. ENAu requires
> more heat to get a Ni/Pb/Sn intermetallic and the gold dissolving in
the
> solder as it rises up the hole, slows down the rate of wetting. There
are
> some options to help this:
> preheat 100 C +10-0, solder temp 235C, speed 1.2m/min, contact time
with
> wave 4 secs, spray fluxer but ensure that flux reaches the top of the
> through holes.
>
> Dougal Stewart,
> Exacta Circuits Scotland
Hi Dougal,
How thick is the gold-board to use with that profile?
Anyway, we need to have more than 4 secs contact time (approx 5-8 secs),
speed of 0.7m/min (upto as slow as 0.4m/min), solder temp 245C, preheat
120C +10-0 and ofcourse a spray application.
/Jan Merstrand
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
|
|
|