Received: |
by ipc.org (Smail3.1.28.1 #2)
id m0vE2HI-0000R6C; Thu, 17 Oct 96 18:55 CDT |
Old-Return-Path: |
|
Date: |
Thu, 17 Oct 1996 19:38:48 -0400 |
Precedence: |
list |
Resent-From: |
|
Message-ID: |
|
X-Status: |
|
Status: |
O |
X-Mailing-List: |
|
TO: |
|
Return-Path: |
<TechNet-request> |
Resent-Message-ID: |
<"fImao.0.i2D.NTiPo"@ipc> |
Subject: |
|
From: |
|
From [log in to unmask] Fri Oct 18 11: |
25:01 1996 |
X-Loop: |
|
Resent-Sender: |
|
Parts/Attachments: |
|
|
Rudy
The unfused tin/lead finish was used very frequently in the 60's and 70's and
if cleaned and stored properly had good solderabability for wave solder
applications using RMA fluxes. I used the finish for at least 10 years with
good results. The only problem was tin/lead slivers and if you use tin, a
major problem is also tin slivers. The factory where I worked had a avg, RH
of 28% and both unfused tin/lead and unfused tin were used and boards were
stored an average of 6 months. The bright or semi bright unfused tin plates
have a good shelf life and In test that I have run were very satisfactory
after two years of storage. The sliver problem was usually alleviated by
building a slight mushroom with the copper and then plating the tin/lead
covering. over the mushroom so that there was no overhang of the tin/lead
that was not supported by copper.
As David mentioned, the use of a thin 0.0002-0.0003 in. of tin/lead plate as
a final finish is not infrequently used for surface mount to provide a flat
land and they are soldered with standard no-clean and RMA fluxes. Good
storage conditions, again, are desirable.
Phi Hinton
[log in to unmask]
***************************************************************************