Received: |
by ipc.org (Smail3.1.28.1 #2)
id m0tm167-0000EhC; Mon, 12 Feb 96 10:27 CST |
Content-Type: |
text/plain; charset="iso-8859-1" |
Old-Return-Path: |
|
Date: |
Mon, 12 Feb 1996 09:34:06 +0100 |
Precedence: |
list |
Resent-From: |
|
Resent-Sender: |
|
Content-Transfer-Encoding: |
quoted-printable |
Status: |
O |
X-Mailing-List: |
|
X-Sender: |
|
TO: |
|
Return-Path: |
|
X-Status: |
|
Resent-Message-ID: |
<"egL15.0.s73.jfs7n"@ipc> |
Subject: |
|
From: |
|
X-Loop: |
|
Mime-Version: |
1.0 |
From [log in to unmask] Tue Feb 13 11: |
37:28 1996 |
Message-Id: |
<v01520d02ad44abd92e42@[129.132.54.198]> |
Parts/Attachments: |
|
|
Hi Andy
The maximum elongation for eutectic solder to failure depends very strong
on the temperatrure and the strain-rate. If you deform solder very fast it
can not endure more than say 2%. If you induce a strain rate below 10 E-4
you can deform solder at room temperature over 100%. Heating the material
to 50°C will ease the problem to a considerable extend.
Guenter Grossmann
|
|
|