| Received: |
by ipc.org (Smail3.1.28.1 #2)
id m0uvXdc-0000NqC; Tue, 27 Aug 96 18:33 CDT |
| Old-Return-Path: |
|
| Date: |
Tue, 27 Aug 96 16:30:51 PST |
| Precedence: |
list |
| From [log in to unmask] Wed Aug 28 09: |
07:17 1996 |
| Resent-Sender: |
|
| X-Status: |
|
| Status: |
O |
| X-Mailing-List: |
|
| TO: |
|
| Return-Path: |
<TechNet-request> |
| Resent-Message-ID: |
<"2dBsD2.0.ExE.JNu8o"@ipc> |
| Subject: |
|
| From: |
|
| Resent-From: |
|
| X-Loop: |
|
| Message-Id: |
|
| Parts/Attachments: |
|
|
Barry,
What process problem are they trying to solve? This sounds strange
that a change to matte would solve any soldermask processing issues?
It might cover them up so you do not see them!
Caution!
______________________________ Reply Separator _________________________________
Subject: assy: matte or glossy soldermask?
Author: [log in to unmask] at corp
Date: 8/27/96 4:09 PM
Greetings!
We are relatively new to the SMT assembly business. Our
vendor wants to switch from a glossy to a matte surface
soldermask to eliminate a process problem on their end.
Are there any issues we need to consider? I seem to recall
a discussion about solder balls hating matte finish.
Thanks
Barry Allen
SED Systems Inc.
[log in to unmask]
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
|
|
|