X400-Content-Type: |
P2-1988 ( 22 ) |
Old-Return-Path: |
|
Date: |
06 Aug 96 08:53:52 -0500 |
Precedence: |
list |
Resent-From: |
|
Conversion: |
Allowed |
Disclose-Recipients: |
Prohibited |
Resent-Sender: |
|
X-Status: |
|
From [log in to unmask] Tue Aug 6 17: |
52:20 1996 |
Priority: |
non-urgent |
Status: |
O |
Content-Return: |
Allowed |
X-Loop: |
|
TO: |
|
X-Mailing-List: |
|
Return-Path: |
<TechNet-request> |
Message-Id: |
<0021732074E70029*/c=us/admd=cwmail/prmd=carrier/o=syracuse/ou=ccmail1/s=Parr/g=Aric/@MHS> |
X400-Recipients: |
non-disclosure; |
Received: |
by ipc.org (Smail3.1.28.1 #2)
id m0unnQF-0000OtC; Tue, 6 Aug 96 09:47 CDT |
X400-Originator: |
|
Resent-Message-ID: |
<"x01r2.0.mF7.Hir1o"@ipc> |
Subject: |
|
From: |
|
Alternate-Recipient: |
Allowed |
X400-Received: |
by /c=us/admd=cwmail/; Relayed; 06 Aug 96 08:53:52 -0500
by mta MTAwltk in /c=us/admd=cwmail/; Relayed;
06 Aug 96 08:53:52 -0500 |
Content-Identifier: |
0021732074E70029 |
X400-Mts-Identifier: |
[/c=us/admd=cwmail/; 0021732074E70029-MTAwltk] |
Parts/Attachments: |
|
|
Try doing a copper purge.
We purge copper from our solder wave by cooling the pot to just above
freezing for 12 (or more) hours. The copper forms 1-3 balls that we
scoop out. This generally reduces copper concentration from .2% to
less than measurable.
This can be done on a weekend.
I don't see why you can't do something similar.
Aric Parr
United Technologies Electronic Controls
______________________________ Reply Separator _________________________________
Subject: FAB: HASL drossing
Author: [log in to unmask] at internet
Date: 8/5/96 2:42 PM
Hello Technet,
We are having difficulty maintaining our HASL pot below 0.25% Cu, even
with 2x daily drossing. The machine is an old vertical Electrovert
with less than easy access.
- Is this 0.25% more critical at assembly than at fab?
- What is the practical USL for copper in HASL?
- How often should metal contaminants be measured?
- Should drossing be done at a constant frequency, or based on panel
loading?
- Are there any studies out there correlating HASL quality with Cu
contamination level?
- Any special recommended procedures or tools?
As always, we appreciate any input.
Joe Felts
PC World, Toronto
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
|
|
|