Mime-Version: |
1.0 |
Content-Type: |
text/plain; charset="us-ascii" |
Old-Return-Path: |
|
Date: |
Fri, 26 Jul 1996 16:33:28 -0500 |
Precedence: |
list |
Resent-From: |
|
Resent-Sender: |
|
X-Status: |
|
Status: |
O |
X-Mailing-List: |
|
X-Sender: |
|
TO: |
|
Return-Path: |
<TechNet-request> |
X-Loop: |
|
From [log in to unmask] Tue Jul 30 11: |
51:13 1996 |
Subject: |
|
From: |
|
Received: |
by ipc.org (Smail3.1.28.1 #2)
id m0ujtPP-0000MxC; Fri, 26 Jul 96 15:22 CDT |
Resent-Message-ID: |
<"QMncC3.0.iwE.PaI-n"@ipc> |
X-Mailer: |
Windows Eudora Light Version 1.5.2 |
Message-Id: |
|
Parts/Attachments: |
|
|
We have been starting to have solderability problems with some electroless
nickel plated pwbs. Nickel has always been a challenge to solder... but we
have been successful until recently by simply doing a pumice scrub prior to
solder stenciling, and by minimizing the time through assembly and into reflow.
There have been a large number of Technet communications on Electroless Ni
and Immersion Au over the last few weeks. We are tying to learn from those
who are having similar problems.
A few topics which were not fully addressed and would be of great value are:
1. Does anyone know of a good test coupon or test method which can be used
to evaluate pwb surface solderability?
2. What role does surface finish play in solderability and will a rough
plated Ni finish have more solderability problems than a smoother finish?
Any help would be appreciated.
Bill Dieffenbacher, Lockheed Martin Control Systems
[log in to unmask] Phone 607-770-2961 Fax 2056
_______________________________________________________________
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************