| Mime-Version: |
1.0 |
| Content-Type: |
text/plain; charset="us-ascii" |
| Old-Return-Path: |
|
| Date: |
Tue, 14 May 1996 21:44:38 +0800 (SST) |
| Precedence: |
list |
| Resent-From: |
|
| Resent-Sender: |
|
| X-Status: |
|
| From [log in to unmask] Thu May 16 12: |
57:33 1996 |
| X-Mailing-List: |
|
| X-Sender: |
|
| TO: |
|
| Return-Path: |
<TechNet-request> |
| Status: |
O |
| Resent-Message-ID: |
<"FfCG.0.4cC.Bq8cn"@ipc> |
| Subject: |
|
| From: |
|
| X-Loop: |
|
| Received: |
by ipc.org (Smail3.1.28.1 #2)
id m0uJKJw-0000CFC; Tue, 14 May 96 08:39 CDT |
| X-Mailer: |
Windows Eudora Light Version 1.5.4 (16) |
| Message-Id: |
|
| Parts/Attachments: |
|
|
>Dear Technet,
>
>Whenever, I'm running a 100% through-hole board, that is densely populated
>with mainly DIP components, and a only few capacitors and resistors., 20 to
>30% of the solder joints are gritty.
>
>It had never happened to board of mixed technology.
>I have sent the solder for lab. analysis, and the result is within the
recommended specification.
>
>The Board is :-
>10 x 10 sq.inch
>4 layers
>
>The wave-solder Machine used :-
>The wave-solder machine used is SEHO 2000 - a full-blown nitrogenous tunnel.
>The solder pot temperature is set at 245 deg.cel or 473 deg.F.
>The top side temperature is measured at about 194 deg.F / 90 deg.C.
>Conveyor speed is set 0.90 metre/minute.
>The solid content of the flux is 1%.
>
>Could anybody advise me why this is happening, and how to solve it. Our
rework operators are touching every gritty joint.
>
>
>Poh Kong Hui
>Nera Electronics
>
|
|
|