agree.  if you have to do it, gold tin eutectic solder?  it depends what
application your operation on (strength, fatigue, etc.etc.).  of  course,
you need full qual to change solder material.  ("tin" finger 1st before
solder it).
fyi.
jk
> It is not recommended. I would first tin the terminals using RMA flux to
> remove the gold. Tin the stranded wire with either RMA or no-clean and
> soak in IPA, then blow off thoroughly and wash with a good saponifier,
> bake dry, and then solder the tinned wires to the tinned terminals with
> the same NC/RMA flux and clean again the same way. Do not use DI water
> first. Clean off (or at least dilute) as much of the flux as you can with
> IPA, then clean with water.
> Otherwise you will have a reaction between the DI water and the
> no-clean/RMA flux (white conductive residue).
> Any flux residues that might remain after cleaning will be negligible.
> Dean
>
> -----Original Message-----
> From: TechNet <[log in to unmask]> On Behalf Of Hernandez, Victor G
> Sent: Friday, March 8, 2024 11:19 AM
> To: [log in to unmask]
> Subject: [TN] Metallurgical Inquiry
>
> ----
> External E-mail --- CAUTION: This email originated from outside GDMS. Do
> not click links or open attachments unless you recognize the sender and
> know the content is safe.
>
> Fellow TechNetters:
>
>     Is it permissible to solder a stranded wire to a gold finger pads with
> either Sn Pb or Pb-free solder?
> Typically, gold fingers are electroplated, hard gold.
> Any chance of galvanic corrosion?
>
> Victor,
>
>
>
>
> Internal Use - Confidential
>