Hi Phil,
I think the dross would be more hazardous than bar solder because it is a
powder that is more difficult to contain, is it more toxic? No. I would
think that both bar solder and tin/lead dross have the same toxicity level.
What I do is keep a pallet with my empty dross buckets back by the wave
solder machine, and when I get about 12-15 buckets I'll call my supplier
for a pick-up. Once it goes through the refining process we usually get a
check for a few thousand dollars.
As a side note, I do use Kleenox when I de-dross the pot to help cut down
on pulling a lot of metal out of the pot, but I don't mind pulling some
metal from the pot in order to introduce virgin bars back into the the pot
to keep the metal percentages in check. You can get too low on tin if you
are too fastidious about pulling ONLY the oxides from the pot.
Steve
On Tue, Aug 28, 2018 at 9:20 AM, Nutting, Phil <[log in to unmask]>
wrote:
> Yes, we still use some tin/lead solder. A question came up recently about
> storing tin/lead dross from a wave solder machine because it was "hazardous
> material". We would want to store it until we had enough material to make
> recycling it cost effective.
>
> How different is dross from raw bar solder of the same alloy?
>
> Phil Nutting | HVP Senior Development Engineer | Excelitas
> Technologies Corp
>
> Lab: +1 978.224.4332 | Office: +1 978.224.4152
> 35 Congress St, Salem, MA 01970 USA
> [log in to unmask]<mailto:[log in to unmask]>
> www.excelitas.com<http://www.excelitas.com/>
>
>
> [Excelitas R_emailsig]
>
>
> Please consider the environment before printing this e-mail.
> ________________________________
> This email message and any attachments are confidential and proprietary to
> Excelitas Technologies Corp. If you are not the intended recipient of this
> message, please inform the sender by replying to this email or sending a
> message to the sender and destroy the message and any attachments. Thank
> you.
>
--
Steve Gregory
Kimco Design and Manufacturing
Process Engineer
(208) 322-0500 Ext. -3133
--
This email and any attachments are only
for use by the intended
recipient(s) and may contain legally privileged,
confidential, proprietary
or otherwise private information. Any
unauthorized use, reproduction,
dissemination, distribution or other
disclosure of the contents of this
e-mail or its attachments is strictly
prohibited. If you have received
this email in error, please notify the
sender immediately and delete the
original.
|