Blue, Orange, Green, Brown, Slate.... Yep... didn't do the same, but worked in it for many years... :-) It was always interesting to see the look on a backhoe operators face when they pull up the colored roots, kind of messy "eh"? And, NO, I'm not from there but I did some work there also...
Later...
Scott Decker – Staff Engineer, PCB Design Services CID+ – Electronic Systems Center
UTC AEROSPACE SYSTEMS
3445 S. 5th Street, Suite 170, Phoenix, AZ 85040 U.S.A.
Tel: 602 308 5957 FAX: 602 243 2347
KE7MWT AKA:PadMasterson
[log in to unmask] www.utcaerospacesystems.com
CONFIDENTIALITY WARNING: This message may contain proprietary and/or privileged information of
UTC Aerospace Systems and its affiliated companies. If you are not the intended recipient please 1) do not disclose, copy,
distribute or use this message or its contents, 2) advise the sender by return e-mail, and 3) delete all copies (including all
attachments) from your computer. Your cooperation is greatly appreciated.
This Document Does Not Contain Export Controlled Technology Or Technical Data.
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Stadem, Richard D
Sent: Monday, April 30, 2018 5:27 AM
To: [log in to unmask]
Subject: [External] Re: [TN] Flux question
LOL. I did live in Canada for 3 years when I was 19,20,21. Worked for Canada Telephone as a lineman, traveling all over the country, coast to coast, repairing phone lines. Lived up northeast of Flin Flon on a Cree Indian reservation. Best three years of my life; I never should have come home.
Odin
From: BEV CHRISTIAN [mailto:[log in to unmask]]
Sent: Thursday, April 26, 2018 7:16 PM
To: TechNet E-Mail Forum; Stadem, Richard D
Subject: RE: [TN] Flux question
😊 I see you use “eh”. Part Canuck?
Bev
Sent from Mail<https://urldefense.proofpoint.com/v2/url?u=https-3A__go.microsoft.com_fwlink_-3FLinkId-3D550986&d=DwIGaQ&c=ilBQI1lupc9Y65XwNblLtw&r=Z5GKU9L_wgbp5uvPzUdN9HWtU4lRZiIaLoTaEwcy40w&m=qgKaQechP0PEoZUdlqZstgvprbYkayl-fmNDqnHlyak&s=Ddl4hO37491yQOYhO_isYXX7C5Cm1kL_aO5130RI0Bo&e=> for Windows 10
From: Stadem, Richard D<mailto:[log in to unmask]>
Sent: Thursday, April 26, 2018 1:19 PM
To: [log in to unmask]<mailto:[log in to unmask]>
Subject: Re: [TN] Flux question
Bev, you anwered at 12:17 my time, and I sent at 12:18 my time.
Then I read your response below.
Great minds think alike, eh?
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of BEV CHRISTIAN
Sent: Thursday, April 26, 2018 12:17 PM
To: [log in to unmask]<mailto:[log in to unmask]>
Subject: Re: [TN] Flux question
Joey,
You probably don’t want to hear this, but… the answer is “it depends”. How marginal is marginal? What is the lead finish? Are the pad connected to a ground plane? What is your reflow profile?
Regards,
Bev
Sent from Mail for Windows 10
From: Jose A Rios
Sent: Thursday, April 26, 2018 1:06 PM
To: [log in to unmask]<mailto:[log in to unmask]>
Subject: [TN] Flux question
Is ROL0 flux an adequate one when faced with having to solder marginally oxidized components. Or should a different flux type be selected. Application is ground based/hi-rel (non flight). Flowdown is J-001 (not space addendum). Thanks….