Bev, you anwered at 12:17 my time, and I sent at 12:18 my time.
Then I read your response below.
Great minds think alike, eh?
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of BEV CHRISTIAN
Sent: Thursday, April 26, 2018 12:17 PM
To: [log in to unmask]
Subject: Re: [TN] Flux question
Joey,
You probably don’t want to hear this, but… the answer is “it depends”. How marginal is marginal? What is the lead finish? Are the pad connected to a ground plane? What is your reflow profile?
Regards,
Bev
Sent from Mail for Windows 10
From: Jose A Rios
Sent: Thursday, April 26, 2018 1:06 PM
To: [log in to unmask]
Subject: [TN] Flux question
Is ROL0 flux an adequate one when faced with having to solder marginally oxidized components. Or should a different flux type be selected. Application is ground based/hi-rel (non flight). Flowdown is J-001 (not space addendum). Thanks….
José (Joey) Ríos, Sr QA Engineer
Mission Assurance Manager
Kavli Institute for Astrophysics & Space Research Massachusetts Institute of Technology [log in to unmask]<mailto:[log in to unmask]>
(617)324-6272
|
|
|