Thanks for the reply Steve.
We had a military customer some 10 years ago specifically call out the Lance Armstrong bands. They did not want anyone working on their product to wear those silicone bands.
My understanding is that the Fitbit bands are made of elastomer material and am not sure what makes that different than silicone. When I look that up, it says that an elastomer is a silicone. The feel of the two are very different.
Many at work wear Fitbit watches. But there are several individuals, one of who is an engineer, that believes any one working on the production floor should not wear one.
I am looking for a definitive answer, but have not been able to find one.
Sue
From: Steve Gregory [mailto:[log in to unmask]]
Sent: Monday, July 17, 2017 4:26 PM
To: TechNet E-Mail Forum <[log in to unmask]>; Sue Powers-Hartman <[log in to unmask]>
Subject: Re: [TN] Fitbit watch band
Hi Sue,
Here is something you might read. It may have something to do with this NASA advisory from a while back...
http://www.spaceref.com/news/viewsr.html?pid=16511
Steve
On Mon, Jul 17, 2017 at 4:03 PM, Sue Powers Hartman <[log in to unmask]<mailto:[log in to unmask]>> wrote:
Several individuals have asked me if the Fitbit watch band is a danger if around the manufacturing of circuit cards, since the band is a type of silicone. Does anyone have an answer to this.
Thank you
--
Steve Gregory
Kimco Design and Manufacturing
Process Engineer
(208) 322-0500 Ext. -3133
[Image removed by sender.]
This email and any attachments are only for use by the intended recipient(s) and may contain legally privileged, confidential, proprietary or otherwise private information. Any unauthorized use, reproduction, dissemination, distribution or other disclosure of the contents of this e-mail or its attachments is strictly prohibited. If you have received this email in error, please notify the sender immediately and delete the original.
|
|
|