Subject:
From:
Theodore J Tontis <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Date:
Fri, 6 Nov 2015 18:49:17 +0000
Content-Type:
text/plain
Parts/Attachments:
text/plain (1 lines)
FYI, 

I was able to pull the book up on Google Scholar for free.  You will not be able to print it but you will be able to read it and search the text for key words and phrases. 

https://books.google.com/books?hl=en&lr=&id=6KHqBwAAQBAJ&oi=fnd&pg=PR15&dq=The+Mechanics+of+Solder+Alloy+Wetting+and+Spreading&ots=0HEzA_ySb7&sig=pkaKBKNSCGNQ6I-agMCkkZTSAkM#v=onepage&q&f=false

Ted T.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Bev Christian
Sent: Friday, October 30, 2015 8:09 PM
To: [log in to unmask]
Subject: Re: [TN] No-wetting on Mini USB (Nickel plating)

One of my favourite books of the industry and I ain't sellin'!  :)

You can buy it for $70 from the publisher.

http://link.springer.com/book/10.1007%2F978-1-4684-1440-0

Bev

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Guy Ramsey
Sent: October 30, 2015 9:05 AM
To: [log in to unmask]
Subject: Re: [TN] No-wetting on Mini USB (Nickel plating)

It is a textbook that was part of the EMPF Bootcamp. I doubt it is in print. You might find a used copy. 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Ioan Tempea
Sent: Friday, October 30, 2015 8:23 AM
To: [log in to unmask]
Subject: Re: [TN] No-wetting on Mini USB (Nickel plating)

Hi Guy,

I've browsed the web for the text you mention, but it only appears under references in several books. Do you have any idea where I can get this particular article from?

Thanks,

Ioan Tempea

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Guy Ramsey
Sent: October-30-15 8:11 AM
To: [log in to unmask]
Subject: Re: [TN] No-wetting on Mini USB (Nickel plating)

Excellent and important point. We did some FA on parts like this. A skilled hand soldering technician can make a very nice looking solder connection that has very poor or non-existent intermetallic. We infer that the intermetallic has formed by the appearance of the low contact angle and wetting, but wetting by surfactant is different from wetting do to "soldering". Well discussed in the text, The Mechanics of Solder Alloy Wetting & Spreading; Yost, Hosking, Frear. Van Hostrand Reinhold press, 1993. 


Guy

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Bev Christian
Sent: Thursday, October 29, 2015 8:10 PM
To: [log in to unmask]
Subject: Re: [TN] No-wetting on Mini USB (Nickel plating)

Deng,
I suggest if you have the time, get the supplier to provide you connectors with a tin or solder plating already on the connection pins.  

About a decade ago almost lost my job over these suckers.  Told my boss that the USB connectors were bare nickel and he brushed it off and we had terrible field problems as a result.
Bev
Blackberry

Opinions expressed are my own and may not represent those of the company I work for.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Deng RongJun
Sent: October 29, 2015 3:33 AM
To: [log in to unmask]
Subject: [TN] No-wetting on Mini USB (Nickel plating)

Hi Technetters

I have got a problem with a SMT type mini USB connector. The four pins contacted shield are no-wetting after reflow soldering.  But can be solder well by iron.
The pins only plated by Nickel, is it possible the oxidation film creating on pin surface and then affect soldering? 

Picture:
https://goo.gl/photos/qap1CBEWzUEJEc5i6

Thanks in advance.
 
RongJun Deng


______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________


______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

ATOM RSS1 RSS2