Au80Sn20 is quite strong and brittle. Works for some applications. Often used
for hermetic soldered lid seals, but they'll make it in very thin wire solder
if you can afford it.
Wayne
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of David Hillman
Sent: Wednesday, April 01, 2015 10:39 AM
To: [log in to unmask]
Subject: Re: [TN] HIGH Temperature Solder
Hi Jeff - here are a couple of other choices:
10Sn88Pb2Ag
1Sn97.5Pb1.5Ag
97Pb3Ag
Nothing wrong with you 90Pb10Sn either. Make sure you select a flux core that
has good thermal stability as your soldering temperatures are much hotter than
what you deal with when using the Sn63Pb37 alloy. Also consider what the
cleaning (or not cleaning) issues you may have to deal with.
Dave Hillman
Rockwell Collins
[log in to unmask]
On Wed, Apr 1, 2015 at 9:20 AM, McGlaughlin, Jeffrey A <
[log in to unmask]> wrote:
> I need to spec a high temperature wire solder for hand soldering. I
> need to have a solidus of greater than 250 degrees C. Is 90Pb10Sn my
> best/only choice or is there something else I should look at?
>
> Jeffrey McGlaughlin, C.I.D.
> Engineering Designer
> Avionics Systems & Tech Refersh
> Office: 614.424.7582| Fax: 614.458.7582
> [log in to unmask]<mailto:[log in to unmask]>
>
> Battelle
> 505 King Avenue
> Columbus Ohio 43201-2693
> http://www.battelle.org<http://www.battelle.org/>
>
> Connect with Battelle
> Facebook<http://www.facebook.com/battelle> | LinkedIn<
> http://www.linkedin.com/company/battelle>
> Twitter<http://www.twitter.com/Battelle> | YouTube<
> http://www.youtube.com/user/battelleinnovations>
>
> This message is intended only for the use of the individual or entity
> to which it is addressed, and may contain information that is
> privileged, confidential and/or otherwise exempt from disclosure under
> applicable law.
> If the reader of this message is not the intended recipient or the
> employee or agent responsible for delivering the message to the
> intended recipient, any disclosure, dissemination, distribution,
> copying or other use of this communication or its substance is
> prohibited. If you have received this communication in error, please
> return to the sender and delete from your computer system.
>
>
>
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or
> [log in to unmask]
> ______________________________________________________________________
>
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|