Hi Victor,
Found this, so NiB must be pretty hard stuff:
https://www.wmdguns.com/
Steve
On Mon, Jan 26, 2015 at 2:23 PM, Victor Hernandez <
[log in to unmask]> wrote:
> Back to the original question about nickel hardness between Ni B and Ni P.
>
> Victor,
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Stadem, Richard D.
> Sent: Monday, January 26, 2015 2:02 PM
> To: [log in to unmask]
> Subject: Re: [TN] Nickel Question
>
> Usually, but not always. Oftentimes a tungsten/nickel/boron finish is
> electroplated instead of the more common chromium, and when electroplated
> it is much harder than the electroless plating (it is generally thicker).
> But this is usually done for mechanical components.
>
> http://www.osti.gov/scitech/biblio/72974-QMzJhC/webviewable/
> http://asterionstc.com/tungsten-nickel-boron-electroplating-system/
>
> But I have never heard of electroplated TNB being used as a circuit board
> finish. I don't think you can solder to it, if that is what you are asking.
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Vladimir Igoshev
> Sent: Monday, January 26, 2015 6:53 AM
> To: [log in to unmask]
> Subject: Re: [TN] Nickel Question
>
> Victor,
>
> Ni-B is also electroless
>
> Vladimir
>
> Sent from my BlackBerry 10 smartphone on the Rogers network.
> Original Message
> From: Victor Hernandez
> Sent: Monday, January 26, 2015 07:49
> To: [log in to unmask]
> Reply To: TechNet E-Mail Forum
> Subject: [TN] Nickel Question
>
> Fellow TechNetters:
>
> Does Ni boron (electroplated process) and Ni Phosphorous (ENIG process)
> have the same hardness?
>
> Victor,
>
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
--
This email and any attachments are only for use by the intended
recipient(s) and may contain legally privileged, confidential, proprietary
or otherwise private information. Any unauthorized use, reproduction,
dissemination, distribution or other disclosure of the contents of this
e-mail or its attachments is strictly prohibited. If you have received this
email in error, please notify the sender immediately and delete the
original.
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|