Jim,
The corner pins are most likely to get bent, but no, it doesn't look like that's the problem. You said there were two failure - are they in the same location? Perhaps the temperature in reflow is a little lower there?
The parts seems a little high on the solder. Is there adhesive or something under the part that is holding it up? Something that could be contributing?
Ben
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Jim West
Sent: Tuesday, November 18, 2014 3:13 PM
To: [log in to unmask]
Subject: EXTERNAL: [TN] Solder defect
Hi all,
Please see attached links. (Thanks Steve) http://stevezeva.homestead.com/IMG00002.jpg
http://stevezeva.homestead.com/IMG00004.jpg
http://stevezeva.homestead.com/IMG00008.jpg
We have recently come across two failures that were the result of one (1) pin not soldered on a 144 pin QFP. Looking at the pictures, you'll see no wetting and the pin embedded in the solder. We could say it's contamination, but we had no issues with any other pins on the QFP. One more thing to add to the troubleshooting, the failure is the same pin (36) on the QFP. Do I have a warping issue? The pin doesn't appear to be bent, but I have not ruled that out until I have better means of verifying. If it's contamination, why only one pin? I would think that I would get at lease the heel or toe, or even the sides to solder, but in this case no wetting. You can see the pin has made contact with the solder due to the indentation. How does this not solder if it has made contact with the solder paste? I'm at a loss and we will probably end up sending this to a lab, but I'm not sure if we will gain anything from a lab??
We are using leaded solder for this application.
Photo IMG00002 and 00004 are from the same failure Photo IMG00008 is the 2nd failure.
Your thoughts?
Thanks,
Jim
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|