Drill after ENIG
Brian
On 10.06.2014 18:26, Henry Rekers wrote:
> Hey there technetters. A while back, I sent a message about enig plating
> contamination in NON-plated holes. I've bounced it back to the board
> shop saying that it is unacceptable, but they claim it is due to 6012
> 3.5.2
> I also think it's unacceptable in the 4552 spec. The design
> documentation clearly states non-plated. It's not plated, just partially
> plated.
>
> Any advice?
>
> Thanks.
> _____________________________________________________________________________________
>
>
> Henry Rekers P. Eng | Schneider Electric | Global Supply Chain |
> Senior Manufacturing Engineer
> Phone: +1-250-652-7100 ext. 7510 | Toll Free: +1-866-466-7627 ext.
> 7510 | Fax: +1-250-544-2390 |
> Email: [log in to unmask] | Site:
> www.schneider-electric.com | Address: 2195 Keating Cross Road,
> Saanichton, BC, Canada, V8M 2A5
> *** Please consider the environment before printing this e-mail
>
> ______________________________________________________________________
> This email has been scanned by the Symantec Email Security.cloud service.
> For more information please contact helpdesk at x2960 or [log in to unmask]
> ______________________________________________________________________
>
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|