Besides hardness lot of other factors affect wearability. Surface
smoothness, ductility and other components of the alloy matrix.
2% cobalt is good starting point .
Anil
-----Original Message-----
From: Joyce Koo [mailto:[log in to unmask]]
Sent: 23 April 2014 20:04
Subject: Re: Thick gold plating
Co.
"All professional skills are mastered by critiqued practice" - by Schon.
Original Message
From: Victor Hernandez
Sent: Wednesday, April 23, 2014 9:55 AM
To: [log in to unmask]
Reply To: TechNet E-Mail Forum
Subject: [TN] Thick gold plating
Fellow TechNetters:
Besides palladium, what other alloys can be added to gold/nickel to
improve hardness/wearability? Is there an IPC dtandard?
Victor,
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|