Joyce Koo <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Joyce Koo <[log in to unmask]>
Date:
Wed, 9 Apr 2014 16:57:57 +0000
Content-Type:
text/plain
Parts/Attachments:
text/plain (31 lines)
Not smelly.

"All professional skills are mastered by critiqued practice" - by Schon.
  Original Message
From: Greg Munie
Sent: Wednesday, April 9, 2014 12:50 PM
To: [log in to unmask]
Reply To: TechNet E-Mail Forum
Subject: [TN] Definition of Sulfur Free


Anyone have a working definition of "sulfur free" as it impacts solderability of silver finishes?

As an old chemist I would expect the definition "sulfur free" could have both a concentration and a time a part can be exposed to that concentration before soldering is impacted.

Any thoughts/assistance is appreciated.

Greg Munie Ph.D.
Director of Design Programs
+1-847-616-7100 tel
+1-847-597-2803 direct
[log in to unmask]<mailto:[log in to unmask]>
www.ipc.org<http://www.ipc.org/>

[cid:[log in to unmask]][http://www.ipc.org/images/shim.gif]<http://www.ipc.org/>

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

ATOM RSS1 RSS2