ENIG with "Hold the G" ?

Bob K?

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Steve Gregory
Sent: Tuesday, October 01, 2013 6:46 PM
To: [log in to unmask]
Subject: Re: [TN] HASL question

Here's one picture:

http://stevezeva.homestead.com/NonWetting.jpg

Look at the left pad and the tarnish that you see there, does that look like
tarnished nickel?

This is after the board was washed. I have places all over the board that
looks like this. 

I'll post a picture of what it looks like after I printed a solder sample
with paste and sent it through the reflow over

Steve 


-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Steve Gregory
Sent: Tuesday, October 1, 2013 4:16 PM
To: [log in to unmask]
Subject: Re: [TN] HASL question

Ahhhh....it's what I figured. I think that's what happened. I'll have
pictures later.

Steve 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Wayne Thayer
Sent: Tuesday, October 1, 2013 4:15 PM
To: [log in to unmask]
Subject: Re: [TN] HASL question

No.  Not unless somebody screwed up.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Steve Gregory
Sent: Tuesday, October 01, 2013 6:11 PM
To: [log in to unmask]
Subject: Re: [TN] HASL question

Hi all,

It's funny that the HASL topic has come up today, because we just ran a
board today that supposedly was lead-free HASL finished, and man it looks
like crap!

Question; does a PCB get nickel before it gets Lead-free HASL'ed?

Steve 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Vladimir Igoshev.
PhD
Sent: Tuesday, October 1, 2013 2:23 PM
To: [log in to unmask]
Subject: Re: [TN] HASL question

Hello Victor,

 It wouldn't solder in a first palce. 

--
Best regards,

Vladimir Igoshev. PhD
mailto:[log in to unmask]

SENTEC Testing Laboratory Inc.
11 Canadian Road, Unit 7.
Scarborough, ON M1R 5G1
Tel: (416) 899-1882
Fax: (905) 882-8812
www.sentec.ca

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________


______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________